Abstract: In order to decrease the degradation rate of magnesium (Mg) alloys for the potential orthopedic applications, manganese-calcium phosphate coatings were prepared on an Mg-Ca-Zn alloy in calcium phosphating solutions with different addition of Mn 2+ . Influence of Mn content on degradation behaviors of phosphate coatings in the simulated body fluid was investigated to obtain the optimum coating. With the increasing Mn addition, the corrosion resistance of the manganese-calcium phosphate coatings was gradually improved. The optimum coating prepared in solution containing 0.05 mol/L Mn 2+ had a uniform and compact microstructure and was composed of MnHPO 4 ·3H 2 O, CaHPO 4 ·2H 2 O, and Ca 3 (PO 4 ) 2 . The electrochemical corrosion test in simulated body fluid revealed that polarization resistance of the optimum coating is 36273 Ωcm 2 , which is about 11 times higher than that of phosphate coating without Mn addition. The optimum coating also showed the most stable surface structure and lowest hydrogen release in the immersion test in simulated body fluid.
Publisher: Elsevier BV
Date: 12-2018
DOI: 10.1016/J.ACTBIO.2018.10.015
Abstract: Zinc (Zn)-based alloys are considered a new class of biodegradable implant materials due to their superior chemical stability and processability compared to biodegradable magnesium (Mg) alloys. In this study, we report a new biodegradable Zn-5Ge alloy with highly desirable mechanical, corrosion, and biological properties. Microstructural characterization revealed the effective grain-refining effect of germanium (Ge) on the Zn alloy. Tensile test results indicated that the hot-rolled Zn-5Ge alloy showed an ultimate tensile strength of 237.0 MPa, a yield strength of 175.1 MPa, and an elongation of 21.6% while as-cast pure Zn showed an ultimate tensile strength of 33.6 MPa, a yield strength of 29.3 MPa, and an elongation of 1.2%. The corrosion rates measured by potentiodynamic polarization tests in Hank's solution in ascending order are: as-cast Zn-5Ge (0.1272 mm/y) < as-cast pure Zn (0.1567 mm/y) < hot-rolled Zn-5Ge (0.2255 mm/y) < hot-rolled pure Zn (0.3057 mm/y). Immersion tests revealed that the degradation rate of as-cast Zn-5Ge is 0.042 mm/y, less than half of that of hot-rolled pure Zn and ∼62% of that of as-cast pure Zn. Moreover, the Zn-5Ge alloy showed excellent in vitro hemocompatibility and the addition of 5% Ge effectively enhanced the hemocompatibility of pure Zn. CCK-8 assay using murine preosteoblast MC3T3-E1 cells indicated that the diluted extracts at a concentration <12.5% of both the as-cast Zn-5Ge alloy and pure Zn showed grade 0 cytotoxicity the diluted extracts at the concentrations of 50% and 25% of Zn-5Ge alloy showed a significantly higher cell viability than those of pure Zn. STATEMENT OF SIGNIFICANCE: Zinc (Zn)-based alloys are currently considered a new class of biodegradable implant materials due to their excellent processability. Here, we report a novel Zn-5Ge alloy with highly desirable mechanical, corrosion and biological properties. The tensile test results indicated that the hot-rolled Zn-5Ge alloy showed an ultimate tensile strength of 237.0 MPa, a yield strength of 175.1 MPa and an elongation of 21.6% while as-cast pure Zn showed an ultimate tensile strength of 33.6 MPa, a yield strength of 29.3 MPa and an elongation of 1.2%. The corrosion rate measured by potentiodynamic polarization tests in Hank's solution in the ascending order is: as-cast Zn-5Ge (0.1272 mm/y) < as-cast pure Zn (0.1567 mm/y) < hot-rolled Zn-5Ge (0.2255 mm/y) < hot-rolled pure Zn (0.3057 mm/y). Immersion tests revealed that the degradation rate of the as-cast Zn-5Ge is 0.042 mm/y, less than half of that of the hot-rolled pure Zn, ∼62% of that of as-cast pure Zn. Moreover, the Zn-5Ge alloy showed excellent in vitro biocompatibility.
Publisher: Hindawi Limited
Date: 2018
DOI: 10.1155/2018/6519310
Abstract: Four nontoxic biological alloys, Mg-0.5Ca-1Sr-4Zr (Alloy 1), Mg-0.5Ca-1Sr-1.5Zr (Alloy 2), Mg-0.5Ca-3Sr-1.5Zr (Alloy 3), and Mg-0.5Ca-1Sr-0.5Sn (Alloy 4), were prepared by vacuum smelting, gravity casting, and hot rolling. The composition and microstructure of the alloys were investigated by optical microscope, X-ray fluorescence spectrometer (XRF), X-ray diffraction (XRD), scanning electron microscope (SEM), and energy dispersion spectroscopy (EDS). The mechanical properties and corrosion behaviors of the alloys in Hank’s solution were studied. Results showed that a large amount of fine and uniformly distributed second-phase particles (Zr, Mg 17 Sr 2 , and CaMgSn) was observed in four alloys obtained after rolling and alloying. The segregation of Zr in alloys was observed in EDS image, and chemical analysis showed that there was macrosegregation of the elements in the alloys. Furthermore, Mg 17 Sr 2 phases in the Mg-0.5Ca-1Sr-0.5Sn alloy homogenized the distribution of CaMgZn phases. The comprehensive mechanical properties of four newly designed rolled alloys were much higher than those of pure Mg, and the compressive strength of the alloys was more than twice as high as that of pure magnesium. The Mg-0.5Ca-1Sr-0.5Sn alloy released the least hydrogen in Hank’s solution, which was lower than that of pure magnesium. Electrochemical test results in Hank’s solution further showed that the Mg-0.5Ca-1Sr-0.5Sn alloy had delayed corrosion and lowest I c o r r which was 25% of that of pure magnesium. Biological experiments results showed that the Mg-0.5Ca-1Sr-0.5Sn alloy had better biocompatibility and optimal potential for bone substitute material.