Abstract: The purpose of this study was to investigate if nickel-titanium instruments with similar designs manufactured by different thermal treatments would exhibit significantly different in vitro behavior. Thirty-six instruments each of ProTaper Universal (PTU F1 Dentsply Maillefer, Ballaigues, Switzerland), ProFile Vortex (PV Dentsply Tulsa Dental Specialties, Tulsa, OK), Vortex Blue (VB, Dentsply Tulsa Dental Specialties), and TYPHOON Infinite Flex NiTi (TYP Clinician's Choice Dental Products, New Milford, CT) (all size 25/.06) were evaluated. Bending resistance, torsion at failure, and dynamic torsional tests were performed with the instruments (n = 12). Analysis of variance and Tukey post hoc tests were applied. Flexibility was significantly higher for TYP compared with the other 3 groups (P < .0001). With respect to the maximum torque at failure, PV group showed the highest resistance to twisting (torsional strength) among the analyzed instruments followed by VB, TYP, and PTU. The TYP group exhibited greater angular deflection at failure compared with the other groups (P .05). The highest mean forces were recorded with PTU (7.02 ± 2.36 N) and the lowest with TYP (1.22 ± 0.40 N). TYP instruments were significantly more flexible than the other instruments tested. The PV group had the highest torsional strength and TYP, despite being the most flexible, showed similar torsional moments to the other instruments, whereas its angular deflection was the highest among the groups.
Publisher: Wiley
Date: 29-04-2018
DOI: 10.1111/IEJ.12768
Abstract: To investigate the surface morphology and electrochemical potential of superelastic (SE), M-Wire (MW) and shape memory technology (SMT) NiTi instruments before and after single clinical use in vivo. A total of 60 ProTaper Universal F2 (PTU-SE), ProTaper Next X2 (PTN-MW), Typhoon (TYP), Hyflex (HF) and Vortex Blue (VB), the last three SMT, and size 25, .06 taper (n = 6 of each type) files were examined. Scanning electron microscopy (SEM), X-ray energy-dispersive spectroscopy (EDS) and electrochemical potential analysis were employed before and after clinical use. Statistical analysis was performed with one-way analysis of variance and Bonferroni's post hoc test. Significance was determined at the 95% confidence level for both tests. SEM observations of new instruments indicated the presence of marks left by the machining process during manufacturing and EDS revealed the existence of an oxide coating on shape memory instruments. After clinical use, the five types were associated with propagation of transverse cracks 3 mm from the tip. The surface oxide layer of TYP, HF and VB instruments had microcracks in multiple directions, whilst TYP and HF had fragmentation in chip form of the oxide layer. EDS analysis demonstrated a significant reduction of the oxide layer in shape memory instruments, except for VB. Electrochemical potentials were higher for shape memory instruments than for M-Wire and superelastic NiTi instruments, respectively (P < 0.05). It appears that shape memory technology NiTi instruments have a dysfunctional oxide layer after clinical use. Additionally, they featured higher electrochemical potential relative to NiTi instruments manufactured from M-Wire, and conventional superelastic NiTi alloy.
Publisher: Elsevier BV
Date: 12-2013
DOI: 10.1016/J.DENTAL.2013.10.004
Abstract: Comparison of physical and mechanical properties of one conventional and a new NiTi wire, which had received an additional thermomechanical treatment. Specimens of both conventional (NiTi) and the new type of wire, called M-Wire (MW), were subjected to tensile and three-point bending tests, Vickers microhardness measurements, and to rotating-bending fatigue tests at a strain-controlled level of 6%. Fracture surfaces were observed by scanning electron microscopy and the non-deformed microstructures by transmission electron microscopy. The thermomechanical treatment applied to produce the M-Wire apparently increased the tensile strength and Vickers microhardness of the material, but its apparent Young modulus was smaller than that of conventionally treated NiTi. The three-point bending tests showed a higher flexibility for MW which also exhibited a significantly higher number of cycles to failure. M-Wire presented mechanical properties that can render endodontic instruments more flexible and fatigue resistant than those made with conventionally processed NiTi wires.
Publisher: Wiley
Date: 12-07-2015
DOI: 10.1111/IEJ.12333
Abstract: To validate torsional analysis, based on finite elements, of WaveOne instruments against in vitro tests and to model the effects of different nickel-titanium (NiTi) materials. WaveOne reciprocating instruments (Small, Primary and Large, n = 8 each, M-Wire) were tested under torsion according to standard ISO 3630-1. Torsional profiles including torque and angle at fracture were determined. Test conditions were reproduced through Finite Element Analysis (FEA) simulations based on micro-CT scans at 10-μm resolution results were compared to experimental data using analysis of variance and two-sided one s le t-tests. The same simulation was performed on virtual instruments with identical geometry and load condition, based on M-Wire or conventional NiTi alloy. Torsional profiles from FEA simulations were in significant agreement with the in vitro results. Therefore, the models developed in this study were accurate and able to provide reliable simulation of the torsional performance. Stock NiTi files under torsional tests had up to 44.9%, 44.9% and 44.1% less flexibility than virtual M-Wire files at small deflections for Small, Primary and Large instruments, respectively. As deflection levels increased, the differences in flexibility between the two sets of simulated instruments decreased until fracture. Stock NiTi instruments had a torsional fracture resistance up to 10.3%, 8.0% and 7.4% lower than the M-Wire instruments, for the Small, Primary and Large file, respectively. M-Wire instruments benefitted primarily through higher material flexibility while still at low deflection levels, compared with conventional NiTi alloy. At fracture, the instruments did not take complete advantage of the enhanced fractural resistance of the M-Wire material, which determines only limited improvements of the torsional performance.