Publisher: Elsevier BV
Date: 10-2014
DOI: 10.1016/J.CARBPOL.2014.05.058
Abstract: This paper reports the plasticisation effect of the ionic liquid, 1-ethyl-3-methylimidazolium acetate ([Emim][OAc]), as compared with the traditionally used plasticiser, glycerol, on the characteristics of starch-based films. For minimising the additional effect of processing, a simple compression moulding process (which involves minimal shear) was used for preparation of starch-based films. The results show that [Emim][OAc] was favourable for plasticisation, i.e., disruption of starch granules (by scanning electron microscopy), and could result in a more amorphous structure in the starch-based materials (by X-ray diffraction and dynamic mechanical analysis). (13)C CP/MAS and SPE/MAS NMR spectroscopy revealed that not only was the crystallinity reduced by [Emim][OAc], but also the amorphous starch present was plasticised to a more mobile form as indicated by the appearance of amorphous starch in the SPE/MAS spectrum. Mechanical results illustrate that, when either glycerol or [Emim][OAc] was used, a higher plasticiser content could contribute to higher flexibility. In spite of the accelerated thermal degradation of starch by [Emim][OAc] as shown by thermogravimetric analysis, the biodegradation study revealed the antimicrobial effect of [Emim][OAc] on the starch-based materials. Considering the high-amylose starch used here which is typically difficult to gelatinise in a traditional plasticiser (water and/or glycerol), [Emim][OAc] is demonstrated to be a promising plasticiser for starch to develop "green" flexible antimicrobial materials for novel applications.
Publisher: American Chemical Society (ACS)
Date: 19-05-2017
Publisher: American Chemical Society (ACS)
Date: 11-04-2017
Publisher: Springer Science and Business Media LLC
Date: 15-06-2017
Publisher: Royal Society of Chemistry (RSC)
Date: 2015
DOI: 10.1039/C5CP01176K
Abstract: This work shows that the starch semi-crystalline structure can be destructured at much reduced temperature in aqueous [C 2 mim][OAc] of certain concentration.
Publisher: Elsevier BV
Date: 04-2013
DOI: 10.1016/J.CARBPOL.2013.01.024
Abstract: This work revealed that the interactions between starch, the ionic liquid 1-ethyl-3-methylimidazolium acetate ([Emim][OAc]), and water might contribute to the phase transition (gelatinization, dissolution, or both) of native starch at reduced temperature. Using mixtures of water and [Emim][OAc] at certain ratios (7.2/1 and 10.8/1 mol/mol), both the gelatinization and dissolution of the starch occur competitively, but also in a synergistic manner. At lower [Emim][OAc] concentration (water/[Emim][OAc] molar ratio≥25.0/1), mainly gelatinization occurs which is slightly impeded by the strong interaction between water and [Emim][OAc] while at higher [Emim][OAc] concentration (water/[Emim][OAc] molar ratio≤2.8/1), the dissolution of starch is the major form of phase transition, possibly restricted by the difficulty of [Emim][OAc] to interact with starch.
Publisher: Elsevier BV
Date: 08-2016
DOI: 10.1016/J.CARBPOL.2016.03.056
Abstract: The focus of this study was on the effects of plasticisers (the ionic liquid 1-ethyl-3-methylimidazolium acetate, or [Emim][OAc] and glycerol) on the changes of starch structure on multiple length scales, and the variation in properties of plasticised starch-based films, during ageing. The films were prepared by a simple melt compression moulding process, followed by storage at different relative humidity (RH) environments. Compared with glycerol, [Emim][OAc] could result in greater homogeneity in [Emim][OAc]-plasticised starch-based films (no gel-like aggregates and less molecular order (crystallites) on the nano-scale). Besides, much weaker starch-starch interactions but stronger starch-[Emim][OAc] interactions at the molecular level led to reduced strength and stiffness but increased flexibility of the films. More importantly, [Emim][OAc] (especially at high content) was revealed to more effectively maintain the plasticised state during ageing than glycerol: the densification (especially in the amorphous regions) was suppressed and the structural characteristics especially on the nano-scale were stabilised (especially at a high RH), presumably due to the suppressed starch molecular interactions by [Emim][OAc] as confirmed by Raman spectroscopy. Such behaviour contributed to stabilised mechanical properties. Nonetheless, the crystallinity and thermal stability of starch-based films with both plasticisers were much less affected by ageing and moisture uptake during storage (42 days), but mostly depended on the plasticiser type and content. As starch is a typical semi-crystalline bio-polymer containing abundant hydroxyl groups and strong hydrogen bonding, the findings here could also be significant in creating materials from other similar biopolymers with tailored sensitivity and properties to the environment.
Publisher: Elsevier BV
Date: 05-2015
DOI: 10.1016/J.CARBPOL.2014.12.072
Abstract: Starch-based films plasticised by an ionic liquid, 1-ethyl-3-methylimidazolium acetate ([Emim][OAc]), were prepared by a simple compression moulding process, facilitated by the strong plasticisation effect of [Emim][OAc]. The effects of amylose content of starch (regular vs. high-amylose maize) and relative humidity (RH) during ageing of the s les on a range of structural and material characteristics were investigated. Surprisingly, plasticisation by [Emim][OAc] made the effect of amylose content insignificant, contrary to most previous studies when other plasticisers were used. In other words, [Emim][OAc] changed the underlying mechanism responsible for mechanical properties from the entanglement of starch macromolecules (mainly amylose), which has been reported as a main responsible factor previously. The crystallinity of the plasticised starch s les was low and thus was unlikely to have a major contribution to the material characteristics, although the amylose content impacted on the crystalline structure and the mobility of amorphous parts in the s les to some extent. Therefore, RH conditioning and thus the s le water content was the major factor influencing the mechanical properties, glass transition temperature, and electrical conductivity of the starch films. This suggests the potential application of ionic liquid-plasticised starch materials in areas where the control of properties by environmental RH is desired.